Green Roofs TPO Waterproof Material

Name

TPO Waterproofing Membrane

Description

TPO waterproofing membrane combines both polypropylene (plastic) and

 ethylene-propylene (rubber) using state-of-the-art polymer manufacturing

 technology.Plasticizer-free TPO membrane deliver long-term flexibility. The result is an ideal commercial waterproofing membrane

 that is reliable, cost effective, environmentally friendly and easy to install. 

Features

1.High UV-resistance and high reflectivity 

2. Excellent weathering characteristics and long-term flexibility

3..High tensile strength and puncture resistance

4.Excellent resistance to harsh chemicals and industrial pollutants

5.Heat or solvent-welding effectively provides seamless roof coverings

Application

1.Subways and tunnels 

2.Roofs of sports complex 

3.Green roofs 

4.Exposed roofs 

5.Steel roofs 

6.Waste land filling yards 

Construction  Method

The method of installing the TPO membrane is identical to that for PVC membranes:

The membrane must be fixed properly and joined by hot-air welding.

The membrane is suitable for both new structures and reconstructions of bitumen roofs 

(blocks of flats, garages, flat roofs etc)

Provides a 15-year warranty for the product

The membrane may be installed directly onto bitumen without having to use a separation

 layer

The membrane offers excellent anti-UV properties.

No.

Test Item

Indicators

Code P

1

The thickness of resin layer above the reinforcement fabric mm≥

0.40

2

Stretching Performance

Maximum Tension N/cm ≥

250

Max.Tension Elongation%≥

15

3

Heating Treatment Size Change Rate%≤

0.5

4

Low-temperature Bending

-40°C No Craze

5

Water Impermeability

0.3Mpa,2h  Water Impermeability

6

Impact Resistance

0.5kg·m , Water Impermeability

7

Anti-static Loada

20kg Water Impermeability

8

Seam Peel Strength  N/mm ≥

3.0

9

Trapezoid Tear Strength  N≥

450

10

Water Absorbing Capacity

(70°C168h)%

After Soaking ≤

4.0

After Airing≥

-0.40

11

Heat aging(80°C)

Time

672h

Appearance

No blisters, cracks, delamination, bonding and holes

Tensile Strength (max. tensile)Retention%≥

90

Elongation Retention %≥

90

Cold Bending

-40°C, No Craze

12

Chemical Resistance

Appearance

No blisters, cracks, delamination, bonding and holes

Tensile Strength (max. tensile)Retention %≥

90

Elongation Retention%≥

90

Cold Bending

-40°C  No Craze

13

Artificial climate accelerating ageing

Time

1500hb

Appearance

No blisters, cracks, delamination, bonding and holes

Tensile Strength (max. tensile)Retention %≥

90

Elongation Retention %≥

90

Cold Bending

-40°C  No Craze